Aluminium Hydroxide for filler

Appearance
White powder
Molecular formula
Al(OH)3
Molecular Weight
78.0
CAS No.
21645-51-2
Bulk Density(g/cm3)
 
Loosed: 1.1
Packed: 1.3
Density(g/cm3)
2.42
Shelf Life
Longer than 2 years.

 
Application:
1.     A kind of special aluminium hydroxide, a white powder, odorless, tasteless, good in dispersity, high whiteness and low iron content, as the execent filler for artificial marble products.  With it artifical marble can be made with perfect brightness, smooth surface, good dirt resistance, abrasion resistance, bump resistance and high structural strength, is ideal filler for modern new-types of building materials and artware.
 
2. Aluminum hydroxide is of high whiteness, moderate hardness, good fluorine retention and compatibleness, strong detergency, stable chemical properties, can be used as toothpaste abradant.
 
3. Different with many flameproof stuffings, aluminum hydroxide micropowder don't produce toxic and corrosive gas when heated to decompose, moreover, absorb heat and release water vapour to make products resistant to flame and self- extingushing. Therefore, adding this product into plastic, rubber and other high-grade materials can bring products good flame resistance and smoke abatement effect, and improve the resistant to creepage, electric arc and abrasion.
 
4. After surface modification treatment, aluminum hydroxide micropowder are of narrow particle size distribution, stable performances, better dispersion property, lower water absorption and oil absorption compared with ordinary aluminum hydroxide micropowder, which enable the stuffing to be increased in products, and reduce process viscosity, strengthen affinity, improve flameproof property, improve antioxidation and mechanical performance. They are used as ideal stuffing for plastic, rubber, artificial marble, and widely used in communication, electronic, biochemical, building material and other fields.
 
In addition, the superfine powder of 1μm can be obtained by some method, with sound particle size distribution and appears spherical crystal. After modification, the conglobation force is reduced and has very strong antioxidation and flame resistance, wider application range.
 
Brand
Chemical Composition %
PH
Absorption of oil ml/100g
Whiteness
Particle size
Moisture
Al(OH)3
SiO2
Fe2O3
Na2O
D50
(um )
+60 mesh
+325 mesh
   %
H-WF-1
99.5
0.08
0.01
0.35
7.5-9.8
50
97
1.1±0.2
0
0.1 max.
0.5
H-WF-2N
99.5
0.08
0.01
0.35
7.5-9.8
50
97
1.4±0.3
0
0.1 max.
0.5
H-WF-8
99.6
0.05
0.02
0.30
7.5-9.8
35
96
2
0
0.5 max.
0.4
H-WF-10
99.6
0.05
0.02
0.30
7.5-9.8
33
96
10±2
0
1.0 max.
0.3
H-WF-14
99.6
0.05
0.02
0.30
7.5-9.8
32
95
15±3
0
12 max.
0.3
H-WF-14-SP
99.6
0.03
0.02
0.20
7.5-9.8
30
95
16±3
0
12 max.
0.3
H-WF-20
99.6
0.05
0.02
0.25
7.5-9.8
32
95
21±3
0
30 max.
0.2
H-WF-25
99.6
0.05
0.02
0.30
7.5-10
32
95
25±5
0
-
0.2
H-WF-25-SP
99.6
0.03
0.02
0.20
7.5-10
30
94
25±5
0
-
0.2
H-WF-25MSP
99.6
0.03
0.02
0.20
7.5-9.8
21
95
25±5
0
-
0.2
H-WF-50-SP
99.6
0.03
0.02
0.20
7.5-10
30
93
50±10
0
-
0.2
H-WF-75
99.6
0.05
0.02
0.25
7.5-10
40
93
85±15
-
-
0.1
H-WF-75-SP
99.6
0.03
0.02
0.20
7.5-10
30
92
85±15
-
-
0.1
H-WF-90
99.6
0.05
0.02
0.25
7.5-10
40
93
100±20
-
-
0.1
H-WF-90-SP
99.6
0.03
0.02
0.20
7.5-10
30
91
95±20
-
-
0.1
 
Aluminium Hydroxide MSDS